Product Features
- Shrink ratio 1.25:1
- Excellent clarity
- High flame resistance
- High temperature resistant to 200℃
- Super physical and chemical properties.
- RoHS and REACH compliant.
- Operating temperature: -65℃~200℃
- Minimum fully recovery temperature: 210℃
- Standard color: Clear
Technical Properties
|
Property |
Requirement |
Test Method |
Typical data |
|
Longitudinal shrinkage |
≤5% |
ASTM D2671 |
≤3% |
|
Tensile strength |
13.8MPa Min. |
ASTM D638 |
≥19MPa |
|
Elongation at break |
150% min. |
ASTM D638 |
≥250% |
|
Tensile strenth after aging(232℃, 168hrs) |
9.7MPa Min. |
ASTM D638 |
≥14MPa |
|
Elongation after aging(225℃, 168hrs) |
100% min. |
ASTM D638 |
≥250% |
|
Heat shock (260℃, 4hrs) |
No crack |
ASTM D2671 |
No crack |
|
Low-temperature flexibility(-65℃, 4hrs) |
No crack |
ASTM D2671 |
No crack |
|
Dielectric voltage withstand |
2500V, 60sec, no breakdown |
ASTM D2671 |
No breakdown |
|
Volume resistivity |
1015Ω.cm min. |
ASTM D876 |
≥1016Ω.cm |
|
Corrosion |
No corrosion |
ASTM D2671 |
No corrosion |
|
Flammability |
VW-1 |
UL224 |
pass |
|
Dielectric constant |
- |
- |
2.1 |
Specification
|
Size mm
|
As supplied (mm) |
After recovered (mm) |
Standard packing (m/pc,m/roll) |
|
|
Inside Diameter (min.) |
Inside Diameter (max.) (max.) |
Wall Thickness (min.) (min.) |
||
|
2.5 |
2.5 |
2.0 |
0.20±0.05 |
100 |
|
3.5 |
3.5 |
2.8 |
0.20±0.05 |
100 |
|
4.7 |
4.7 |
3.8 |
0.20±0.05 |
1.0 |
|
5.5 |
5.5 |
4.5 |
0.20±0.05 |
1.0 |
|
7 |
7 |
5.6 |
0.20±0.05 |
1.0 |
|
9 |
9 |
7.5 |
0.25±0.05 |
1.0 |
|
11.5 |
11.5 |
9.3 |
0.30±0.05 |
1.0 |
|
14.5 |
14.5 |
11.7 |
0.35±0.05 |
1.0 |
|
19 |
19 |
15.3 |
0.35±0.05 |
1.0 |
|
24 |
24 |
19.3 |
0.40±0.10 |
1.0 |
|
28 |
28 |
22.5 |
0.40±0.10 |
1.0 |
|
35 |
35 |
28.1 |
0.40±0.10 |
1.0 |
|
44 |
44 |
36.1 |
0.45±0.10 |
1.0 |
|
54 |
54 |
43.3 |
0.50±0.10 |
1.0 |
|
66 |
66 |
52.9 |
0.50±0.10 |
1.0 |
|
78 |
78 |
62.5 |
0.50±0.10 |
1.0 |
|
90 |
90 |
72.1 |
0.50±0.10 |
1.0 |
|
103 |
103 |
82.5 |
0.50±0.10 |
1.0 |
|
120 |
120 |
105 |
0.60±0.10 |
1.0 |